Low-Spatter H10mn2moa Saw Wire with Excellent Crack Resistance for Bridge Construction

• Customization: Available
• Type: Rolling Wire
• Material: Stainless Steel
• Model NO.: HH-H10Mn2
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: >20mm
• Specification: 0.8; 1.0; 1.2; 1.6
• Trademark: Honglu
• Origin: Anhui, China
• HS Code: 7505220000
• Production Capacity: 200000 Tons/Year

Product Description

Detailed Photos

Product Parameters

Mechanical Properties of the Molten Metal:

sports event	tensile strength Rm/MPa	yield strength ReL/Rp0.2MPa	elongation   A%
standard value	490-670	>=490	>=18
example value	564	459	29

Versatile Uses: Ideal for the automatic submerged arc welding of both carbon and low alloy steel, matching the same strength level. Perfectly suited for applications in the construction of ships, petrochemical plants, and boilers, among others.

Distinguishing Characteristics: HH-H10Mn2 is a premium copper-plated, non-alloy submerged arc welding wire, paired with SJ101 flux that ensures exceptional welding process performance. It creates beautifully shaped weld channels, is easy to deslag, and delivers impressive low-temperature impact toughness.

Chemical Composition of Welding Wire: Composition (Mass Fraction) 100%

sports event	C	Mn	Si	S	P	Cr	Ni	Cu
standard value	<=0.12	1.50-1.90	<=0.07	<=0.030	<=0.030	<=0.20	<=0.30	<=0.35
example value	0.11	1.65	0.05	0.017	0.022	0.022	0.02	0.116

Important Precautions:
1. Ensure the flux is properly baked at a temperature range of 250-400 ºC for 1-2 hours. The welding wire should be kept dry and free from oil and rust before use.
2. Prior to welding, clean the surface to remove any rust, oil, water, and other impurities.
3. Maintain sulfur content of the flux at <= 0.050% and phosphorus content at <= 0.060% to ensure quality.