MIG Mag H10mn2 Submerged Arc Welding Wire Saw Wire for Construction Welding

• Customization: Available
• Type: Rolling Wire
• Material: Stainless Steel
• Model NO.: HH-H10Mn2
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: >20mm
• OEM & ODM: Accepted
• Handover: Negotiable; Around 30-35 Days
• Certificate: ISO 9001; CE; RoHS; Reach; OHSAS
• Annual Production Capacity: 200000 Tons
• Specification: 0.8; 1.0; 1.2; 1.6
• Trademark: Honglu
• Origin: Anhui, China
• HS Code: 7505220000
• Production Capacity: 200000 Tons/Year
• Package Size: 800.00cm * 600.00cm * 600.00cm
• Package Gross Weight: 1000.000kg

Product Description

Detailed Photos

Product Parameters

Mechanical Marvels of the Molten Metal:

sports event	tensile strength Rm/MPa	yield strength ReL/Rp0.2MPa	elongation   A%
standard value	490-670	>=490	>=18
example value	564	459	29

Diverse Applications: This remarkable product is the ultimate choice for automatic submerged arc welding of carbon and low alloy steel, delivering a seamless match in strength levels. It is the quintessential solution for the most demanding applications such as shipbuilding, petrochemical plant construction, and boiler manufacturing. With this product, you ensure reliability and unparalleled performance in the most challenging and demanding environments.

Unique Features that Set Us Apart: The HH-H10Mn2 is recognized as a top-tier, copper-plated, non-alloy submerged arc welding wire. Perfectly paired with SJ101 flux, it promises exceptional welding performance. This dynamic duo creates aesthetically pleasing weld channels, allows for effortless slag removal, and boasts impressive low-temperature impact toughness, making it the preferred choice for discerning professionals.

Precise Chemical Composition of the Welding Wire: Composition (Mass Fraction) Achieving 100% Purity

sports event	C	Mn	Si	S	P	Cr	Ni	Cu
standard value	<=0.12	1.50-1.90	<=0.07	<=0.030	<=0.030	<=0.20	<=0.30	<=0.35
example value	0.11	1.65	0.05	0.017	0.022	0.022	0.02	0.116

Critical Safety Precautions:
1. The flux must be diligently baked within a temperature range of 250-400 ºC for 1-2 hours to maintain its optimal properties. Ensure the welding wire remains pristine-dry, free of oil, and rust-free-before its application.
2. For the best results, ensure surfaces are meticulously cleaned of rust, oil, water, and other contaminants prior to welding.
3. Maintain the sulfur content of the flux at <= 0.050% and phosphorus content at <= 0.060% to guarantee superior quality output and exceptional performance.