Copper Coated Saw Wires H10mn2 Welding Wire for High Strength Steel Welding

• Customization: Available
• Type: Rolling Wire
• Material: Stainless Steel
• Model NO.: HH-H10Mn2
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: >20mm
• Specification: 0.8; 1.0; 1.2; 1.6
• Trademark: Honglu
• Origin: Anhui, China
• HS Code: 7505220000
• Production Capacity: 200000 Tons/Year

Product Description

Detailed Photos

Product Parameters

Mechanical Properties of the Molten Metal:

sports event	tensile strength Rm/MPa	yield strength ReL/Rp0.2MPa	elongation   A%
standard value	490-670	>=490	>=18
example value	564	459	29

Uses: This top-quality welding wire is ideally suited for the automatic submerged arc welding of carbon steel and low alloy steel, designed to deliver an equivalent corresponding strength level. Perfect for use in demanding sectors such as shipbuilding, petrochemicals, and boiler manufacturing.

Characteristics: Introducing HH-H10Mn2, an exceptional copper-plated, non-alloy submerged arc welding wire. Paired with SJ101 flux, it offers an outstanding welding process performance. You'll appreciate its beautifully shaped weld channels, easy deslagging, and remarkable low-temperature impact toughness.

Chemical Composition of Welding Wire: (Mass Fraction) 100%

sports event	C	Mn	Si	S	P	Cr	Ni	Cu
standard value	<=0.12	1.50-1.90	<=0.07	<=0.030	<=0.030	<=0.20	<=0.30	<=0.35
example value	0.11	1.65	0.05	0.017	0.022	0.022	0.02	0.116

Precautions:
1. To ensure optimal flux performance, bake it at a temperature range of 250-400 ºC for 1-2 hours. Ensure the welding wire is kept in a dry, oil-free, and rust-free condition before use.
2. Prior to welding, perform telding to thoroughly remove rust, oil, water, and any other impurities.
3. Maintain strict control with sulfur content of flux at <= 0.050% and phosphorus content at <= 0.060%.