Reliable Welding Wire for Ships and Bridges with Wind Speed Limitations Gas-Shielded Solid Wire Submerged Arc Welding Wire Gas-Shielded Flux-Cored Wire

• Customization: Available
• Type: Rolling Wire
• Material: CO2
• Model NO.: Flux Cored Wire
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: >20mm
• Feature: Applied in Industries
• Uses: Ships, Bridges, Marine Engineering, Steel Structu
• Wind Speed Limitation: Less Than or on 1.0m/S
• Shielding Gas: CO2
• Transport Package: Spool+Carton+ Pallet
• Specification: 0.8; 1.0; 1.2; 1.6
• Trademark: Honglu
• Origin: Anhui, China
• HS Code: 7505220000
• Production Capacity: 200000 Tons/Year
• Package Size: 112.00cm * 82.00cm * 84.00cm
• Package Gross Weight: 1750.550kg

Product Description

Product Description

Type	Rolling Wire
Material	500MPa grade carbon steel wire
Flux Containing	Not Containing Flux
Extended Length:	>20mm
Shielding Gas	CO2
Sep	0.8, 1.0, 1.2,1.6
Rm/MPa	490-670
ReL/Rp0.2MPa	>=420

Detailed Photos

Product Parameters

sports event	tensile strength Rm/MPa	yield strength ReL/Rp0.2MPa	elongation   A%
standard value	490-670	>=420	>=20
example value	560	450	26

Uses: Our top-tier Honglu Welding Wire excels in handling welding operations across various strength-level carbon steels and low alloy steel structures. This versatile, high-performance solution finds its ideal applications in industries such as construction machinery, shipbuilding, vehicle manufacturing, and the petrochemical sector. Secure robust and reliable welds every time with our premium welding solution, ensuring durability and uncompromised quality.

Characteristics: The HH-50S-6 wire offers an exceptional solution for welding 500MPa carbon steel. Utilizing CO2 gas shielded welding, it efficiently minimizes spatter while ensuring welds are beautifully shaped. Achieve high deposition efficiency with minimal sensitivity to porosity. Benefit from an all-position welding process that consistently delivers outstanding results, making every project a success.

Mechanical properties of the molten metal:(CO2)

sports event	C	Mu	Si	S	P	Ni	Cr	Mo	V	Cu
standard value	0.06-0.15	1.40-1.85	0.80-1.15	<=0.025	<=0.025	<=0.15	<=0.15	<=0.15	<=0.03	<=0.50
example value	0.08	1.50	0.89	0.012	0.013	0.03	0.02	0.002	0.003	0.11

Precautions:
1. Before welding, it is crucial to meticulously remove rust, oil, water, and any impurities from the weldment. This step is essential to prevent defects and ensure optimal welding results, achieving the highest quality standards.
2. The energy of the welding wire significantly impacts the weld's mechanical properties. For structural components of greater importance, employing smaller wire energy is recommended to ensure enhanced integrity and superior performance.